1. The quality of heat treatment of aluminum extrusion die directly affects the service life of the extrusion die. Quenching is to improve the hardness of the mold, and repeated tempering is to improve the toughness of the mold and stabilize the internal structure. The hardness value of mold heat treatment is specified: large aluminum extrusion die (F>500mm), HRC45-48; Cetakan sedang (F300 ~ 500mm), HRC47-50; Ekstrusi kecil mati (f<300mm), HRC48-51; Three points are tested on the same plane of a set of molds, and the hardness value of each point should be qualified within the specified range.
2. Perhatian khusus harus diberikan pada beberapa titik dalam proses perlakuan panas ekstrusi die:
A. Kecepatan pemanasan dari bagian suhu - tinggi harus cepat, dan waktu penahanan tidak boleh terlalu lama, sehingga mencegah ekstrusi mati karena terlalu panas atau terlalu panas, {3}- {{3} {{2} {{3} {{3} {{3} yang terlalu panas, dana.
B. Setelah pendinginan, ekstrusi aluminium die harus dimatikan dalam waktu untuk mencegah retakan;
C. Ketika kekerasan die ekstrusi ditemukan tidak mencukupi atau tidak merata setelah perlakuan panas, anil harus dilakukan, dan perlakuan panas harus kembali - dilakukan sesuai dengan proses (ketika nilai kekerasan adalah
D. Untuk cetakan ekstrusi aluminium besar atau cetakan jadi dengan rongga kompleks, stres - meringankan proses tempering harus ditambahkan (untuk menghilangkan pemrosesan listrik dan stres pemesinan, yaitu untuk menghilangkan stres termal dan stres struktur mikro);
e. Suhu minyak pendinginan cetakan harus 100 derajat untuk memastikan efek pendinginan.