1. The heat treatment quality of the aluminum extrusion die directly affects the service life of the extrusion die. The die is hardened by "+" tempering several times to reach the hardness requirements. Quenching is to improve the hardness of the die, and multiple tempering is to improve the toughness of the die and stabilize the internal organization. The hardness value of the die heat treatment is specified as follows: large aluminum extrusion die (F>500mm), HRC45-48; Cetakan sedang (F300~500mm), HRC47-50; Die ekstrusi kecil (F<300mm), hrc48-51;="" test="" three="" points="" on="" the="" same="" plane="" of="" a="" set="" of="" molds,="" and="" the="" hardness="" values="" of="" each="" point="" should="" be="" qualified="" within="" the="" specified="">
2. Perhatian khusus harus diberikan pada poin-poin berikut dalam proses perlakuan panas dari cetakan ekstrusi:
sebuah. Laju pemanasan bagian suhu tinggi harus cepat, dan waktu penahanan tidak boleh terlalu lama, untuk mencegah cetakan ekstrusi yang terlalu panas atau terlalu panas. Butir kasar -- yang terlalu panas, elemen titik leleh rendah -- yang terbakar berlebihan, dan inklusi akan larut;
b. Temper ekstrusi aluminium mati tepat waktu setelah pendinginan untuk mencegah retak;
c. Ketika kekerasan die ekstrusi ditemukan tidak mencukupi atau tidak merata setelah perlakuan panas, itu harus dianil, dan perlakuan panas harus dilakukan lagi sesuai dengan proses (ketika nilai kekerasan kurang dari HRC35, anil tidak diperbolehkan, dan perlakuan panas dilakukan secara langsung);
d. Untuk die ekstrusi aluminium besar atau die selesai dengan rongga kompleks, pengurangan stres dan proses temper harus ditambahkan (untuk menghilangkan pemesinan listrik dan tekanan pemesinan, yaitu untuk menghilangkan stres termal dan stres organisasi);
e. Haruskah suhu minyak pendinginan mati? 100 derajat untuk memastikan efek pendinginan.